First of all, let’s talk about the classification of ceramics, which are divided into: daily-use ceramics, artistic ceramics, sanitary ceramics, architectural ceramics, etc. We mainly talk about sanitary ceramics. LORY sanitary ceramics products are of high quality and conform to the “Sanitary Ceramics The qualified product of the national standard GB 6952-2005 “,has the characteristics of high cost performance.
In order to enable you to better use LORY sanitary ceramic products and help you understand the relevant knowledge of sanitary ceramics. At the same time, sanitary manufacturers also want to spread and popularize the knowledge of sanitary products. We explain some common sanitary ceramic products to you in concise text form. LORY sanitary ceramic products are all high-temperature ceramics fired at a high temperature of 1280°C, which have the advantages of high temperature resistance, wear resistance, good stain resistance, easy cleaning, and non-absorbent.
1.What are the advantages of high temperature ceramics:
Temperature: The firing temperature of high temperature porcelain is above 1200°C
Color: the color of high temperature porcelain is more full, delicate and crystal clear
Hand feel: high temperature porcelain is smooth and delicate
Sound: high temperature porcelain is more crisp
Texture: High-temperature porcelain has a stronger hardness
The water absorption rate of high-temperature ceramics is less than 0.2%. The product is easy to clean and will not absorb odors, and there will be no cracks on the glazed surface and local water leakage.
Its production and delivery process is as follows: raw materials – mold – grouting molding – glaze spraying – firing – appearance, glaze, deformation inspection and repair (according to the national standard GB 6952-2005) – accessories installation – water leakage inspection , Flushing performance inspection – qualified finished product packaging – leaving the factory.
Since ceramic products are semi-manufactured products, fired from mud at high temperature, they are easily affected by uncontrollable factors such as kiln temperature control and natural climate, so their evaluation has certain characteristics. LORY sanitary ceramic products are produced and inspected in strict accordance with the “National Standard for Sanitary Ceramics GB 6952-2005”, and the quality of our products are all high-quality products that exceed this standard. Due to the difficult manufacturing process and large volume of sanitary ceramic products, after being fired at a high temperature of 1280°C, some toilets may have air holes and small holes on the inner wall of the water tank, the bottom of the water tank, the toilet base, the basin, or on the surface of the back of the porcelain body Cracks (also known as fire cracks).
A similar phenomenon will also appear on the bottom or back of individual squatting pans, basins, urinals and other ceramic products. We will use “plastic steel clay”, “plastic steel slurry” or “other professional clay” for repairs during quality inspection deal with.
There are very few tiny brown eyes or small bags on the glaze of individual ceramic products. These are normal and unavoidable phenomena. This is by no means a quality problem, nor is it a sign of defective products. These will not affect the appearance or use at all, and there will be absolutely no water leakage, and there will be absolutely no worries in the future. This is within the allowable range of the national quality standard (you can check the “National Standard for Sanitary Ceramics GB 6952-2005” online), and consumers can use it with confidence.
So you don’t need to worry about the phenomenon of fire cracking. For ceramic products fired at a high temperature of 1280°C, some fire cracking is considered normal and will not affect the use. Please rest assured.
Let me share with you the cleaning and maintenance methods of ceramic products.
1. General products can reduce the use of cleaning agents. Please do not use detergent in the water tank. Because chlorine-containing cleaning agents will cause harm to the fittings in the water tank and accelerate aging, resulting in clogging and poor flushing;
2. Neutral detergent should be used to clean the ceramic glaze. The use of strong or abrasive cleaning agents will damage the glazed surface of ceramics. Once the glazed surface is damaged, it is prone to problems such as adhesion, dirt, water absorption, deformation, and discoloration;
3. Do not use nylon brush or scouring pad to clean the ceramic glaze, because it will cause wear to the ceramic surface;
4. Avoid direct impact of hard objects on the surface of the product. Do not pour strong and corrosive liquids into ceramic products, so as not to damage the glaze. If these situations are not paid attention to, the problems caused by them are all man-made damages, which are not included in the after-sales quality problems.
The above is the general knowledge of some national standard sanitary ceramic products. I hope that sellers and consumers can correctly understand LORY sanitary ceramic products. We will use our greatest efforts to improve product quality and serve you sincerely.